Improving flotation separation efficiency of quartz-coal mixtures by using polyethylene oxide

CIM Journal, Vol. 5, No. 1, 2014

H. Wang and M. Cao
Department of Chemical & Materials Engineering, University of Alberta, Edmonton, Alberta, Canada

J.-C. Sztuke and A. Stradling
Applied Research & Technology, Teck Metals Limited, Trail, British Columbia, Canada

Z. Xu and Q. Liu
Department of Chemical & Materials Engineering, University of Alberta, Edmonton, Alberta, Canada

Wash water and polyethylene oxide (PEO) were used in the flotation of quartz and coal. Wash water decreased entrainment of –15 μm quartz. The optimum superficial wash water rate was 0.05 cm/s. PEO also lowered entrainment. The combination of wash water and PEO led to a slight further reduction in entrainment. For 1:1 mixtures of –15 μm quartz and –300 μm oxidized coal, the combined use of wash water (0.05 cm/s) and PEO increased the separation efficiency from approximately 30% to > 70%, whereas wash water alone at 0.05 cm/s did not lead to a discernible increase.

Résumé: L’eau de lavage et le polyéthylène oxyde (PEOX) ont été utilisés dans la flottation du quartz et du charbon. L’eau de lavage a diminué l’entraînement du quartz -15 μm. Le taux optimal d’eau superficielle de lavage était de 0,05 cm/s. Le PEOX a aussi diminué l’entraînement. La combinaison de l’eau de lavage et du PEOX a produit une légère réduction supplémentaire d’entraînement. Pour des mélanges 1:1 de quartz -15 μm et de charbon oxydé -300 μm, l’utilisation combinée d’eau de lavage (0,05 cm/s) et de PEOX a augmenté l’efficacité de séparation d’environ 30 % à plus de 70 %, alors que l’eau de lavage seule à un taux de 0,05 cm/s n’a pas donnée une augmentation discernable.

Keywords: Polyethylene oxide, Coal flotation, Quartz, Entrainment